Retardation substrate, method of manufacturing the same, and liquid crystal display

ABSTRACT

A retardation layer that includes regions causing different retardations can be manufactured easily. A retardation substrate includes a substrate and a solidified liquid crystal layer supported by the substrate. The solidified liquid crystal layer includes first to third regions. The first to third regions re arranged on the substrate and different in degree of orientation of mesogens.

CROSS REFERENCE TO RELATED APPLICATIONS

This is a Continuation Application of U.S. patent application Ser. No. 12/318,869 filed Jan. 9, 2009, which is a Continuation Application of International Application No. PCT/JP2008/052437, filed Feb. 14, 2008, which was published under PCT Article 21 (2) in Japanese, the contents of both of which are incorporated herein by reference.

This application is based upon and claims the benefit of priority from prior Japanese Patent Applications No. 2007-036148, filed Feb. 16, 2007; and No. 2007-242179, filed Sep. 19, 2007, the entire contents of both of which are incorporated herein by reference.

BACKGROUND OF THE INVENTION

1. Field of the Invention

The present invention relates to an optical technique that can be applied, for example, to a display such as liquid crystal display.

2. Description of the Related Art

Liquid crystal displays have characteristics of thin-shaped, lightweight and low power consumption. Thus, in recent years, their application to mobile devices and stationary equipments such as television receivers increases rapidly.

In order to make it possible for a liquid crystal display to display a multi-colored image, a color filter is utilized. For example, in a transmissive or reflective liquid crystal display that can display a multi-colored image, a color filter including red, green and blue coloring layers is utilized in most cases. On the other hand, in a semi-transparent liquid crystal display that can display a multi-colored image, a color filter including red, green and blue coloring layers for transmissive display and red, green and blue coloring layers for reflective display is utilized in most cases.

Many liquid crystal displays include a retardation film. For example, in a liquid crystal display of a television receiver, a retardation film is utilized in combination with a linearly polarizing film in order to display an image that can be easily recognized regardless of the viewing direction. On the other hand, in a reflective or semi-transparent liquid crystal display, an absorption-type circularly polarizing plate including a quarter-wave plate or a combination of a quarter-wave plate and a half-wave plate as a retardation film is utilized in order to achieve an excellent visibility under a high-luminance light source such as sun.

However, in spite of the fact that the red, green and blue pixels are different in wavelength range of display color from one another, the retardation of a retardation film is usually even throughout its surface. For this reason, it is difficult to adopt optimal designs into all the pixels different in display color.

To be more specific, each of the retardation of a liquid crystal layer and the retardation of a retardation film has wavelength dispersion. For this reason, when employing a design for sufficiently compensating the retardation of a liquid crystal cell using a retardation film at pixels that display a certain color, the retardation film may insufficiently compensate the retardation of a liquid crystal cell at pixels that display other colors.

Similarly, in the case where a quarter-wave plate, which causes a retardation by a quarter of a wavelength (λ/4) at a center wavelength of green wavelength range, for example, about 550 nm, is combined with a linearly polarizing plate to be used as a circularly polarizing plate, even when the refractive index anisotropy, i.e., birefringence Δn of the quarter-wave plate is almost uniform throughout the wavelength range of visible rays, a retardation greater than λ/4 will be caused within a blue wavelength range having a center wavelength of, for example, about 450 nm. Also, a retardation smaller than λ/4 will be caused within a red wavelength range having a center wavelength of, for example, about 630 nm. Thus, when the circularly polarizing plate is irradiated with blue and red lights as natural lights, the transmitted light will be not a circularly polarized light but an elliptically polarized light. In fact, since the birefringence is greater on the short-wavelength's side of the visible range, i.e., within the blue wavelength range and is smaller on the long-wavelength's side of the visible range, i.e., within the red wavelength range, this problem is often more serious.

JP-A 2005-24919 and JP-A 2006-85130 describe as a retardation layer a solidified liquid crystal layer that includes regions having different thickness, i.e., regions causing different retardations.

Specifically, JP-A 2005-24919 describes that a color filter layer composed of red, green and blue coloring layers different in thickness is formed, and a solidified liquid crystal layer is formed on the color filter layer. The solidified liquid crystal layer is obtained by coating an alignment layer with a coating solution containing photo-polymerizing liquid crystal compound and irradiating the coated film with ultraviolet rays.

According to this method, due to the relief structure that the coloring layers produces on the surface of the color filter layer, a solidified liquid crystal layer thicker at a position of the thinner coloring layer and thinner at a position of the thicker coloring layer can be obtained. That is, a solidified liquid crystal layer different in thickness among pixels that displays different colors can be obtained. In other words, a solidified liquid crystal layer including regions that cause different retardations can be obtained.

JP-A 2006-85130 describes a semi-transparent liquid crystal display that includes a color filter layer and a solidified liquid crystal layer. In this liquid crystal display, each coloring layer of the color filter layer is thicker at the transmissive portions of pixels and thinner at the reflective portion of the pixels. That is, the surface of the color filter layer is provided with a relief structure. The solidified liquid crystal layer is obtained by forming a polyimide layer on the surface of the color filter layer provided with the relief structure, performing a rubbing process on the whole surface of the polyimide layer, coating the polyimide layer with ultraviolet-curing liquid crystal monomer, and irradiating the coated layer with ultraviolet rays. Alternatively, coating the surface of the color filter layer with a liquid crystal polymer and subjecting the whole of the coated film to a photo-alignment process obtain the solidified liquid crystal layer. The solidified liquid crystal layer thus obtained is thinner at the transmissive portions of pixels and thicker at the reflective portions of the pixels. That is, according to the method, a solidified liquid crystal layer that includes regions causing different retardations can be obtained.

However, according to the technique described in JP-A 2005-24919, it is necessary to accurately adjust the differences in thickness among the coloring layers. Similarly, according to the technique described in JP-A 2006-85130, it is necessary to accurately adjust the difference between the thickness of the coloring layer at the reflective portion and the thickness of the coloring layer at the transmissive portion. For this reason, when the above-described techniques are employed, the design for the color filter layer is limited or the degree of difficulty in manufacturing the color filter layer increases. Therefore, in order to achieve the design thickness at each region of the solidified liquid crystal layer, it is necessary to consider various factors such as flowability of a coating solution and a shrinkage ratio of the coated film.

BRIEF SUMMARY OF THE INVENTION

An object of the present invention is to make it possible to easily manufacture a retardation layer that includes regions causing different retardations.

According to a first aspect of the present invention, there is provided a retardation substrate comprising a substrate, and a solidified liquid crystal layer supported by the substrate and including first to third regions, the first to third regions being arranged on the substrate and different in degree of orientation of mesogens.

According to a second aspect of the present invention, there is provided a liquid crystal display comprising first and second substrates facing each other, a liquid crystal layer interposed between the first and second substrates, a solidified liquid crystal layer supported by a main surface of the first substrate that faces the second substrate and including first to third regions, the first to third regions being arranged on the substrate and different in degree of orientation of mesogens, and a color filter layer supported between the first and second substrates by the first or second substrate and including first to third coloring layers, the first to third coloring layers being different in absorption spectrum and facing the first to third regions, respectively.

According to a third aspect of the present invention, there is provided a method of manufacturing a retardation substrate, comprising forming a solidified liquid crystal layer on a substrate, forming the solidified liquid crystal layer including forming on the substrate a liquid crystal material layer including a photo-polymerizing or photo-crosslinking thermotropic liquid crystal compound, mesogens of the thermotropic liquid crystal compound forming an orientated structure, irradiating at least two regions of the liquid crystal material layer with light at different exposure values to form in the liquid crystal material layer a first region including a polymerization or crosslinking product of the thermotropic liquid crystal compound, a second region including the polymerization or crosslinking product and the thermotropic liquid crystal compound as an unreacted compound and lower in a content of the thermotropic liquid crystal compound than the first region, and a third region including the unreacted compound and lower in a content of the thermotropic liquid crystal compound than the second region, thereafter, heating the liquid crystal material layer to a temperature equal to or higher than a phase transition temperature at which the thermotropic liquid crystal compound changes from a liquid crystal phase to an isotropic phase to lower degree of orientation of mesogens at least in the second and third regions, and causing polymerization and/or crosslinking of the unreacted compound while the degree of orientation is kept lowered.

BRIEF DESCRIPTION OF THE SEVERAL VIEWS OF THE DRAWING

FIG. 1 is a perspective view schematically showing a retardation substrate according to an embodiment of the present invention;

FIG. 2 is a sectional view taken along the line II-II of the retardation substrate shown in FIG. 1;

FIG. 3 is a sectional view schematically showing an example of a method of forming a solidified liquid crystal layer;

FIG. 4 is a sectional view schematically showing an example of a method of forming a solidified liquid crystal layer;

FIG. 5 is a sectional view schematically showing a retardation substrate according to a modified example;

FIG. 6 is a sectional view schematically showing a solidified liquid crystal layer according to an example;

FIG. 7 is a sectional view schematically showing a solidified liquid crystal layer according to another example; and

FIG. 8 is an example of a liquid crystal display that can be manufactured using the retardation substrate shown in FIGS. 1 and 2.

DETAILED DESCRIPTION OF THE INVENTION

An embodiment of the present invention will be described below with reference to the accompanying drawings. Note that the same reference numerals in the drawings denote components that achieve the same or similar functions, and a repetitive explanation thereof will be omitted.

FIG. 1 is a perspective view schematically showing a retardation substrate according to an embodiment of the present invention. FIG. 2 is a sectional view taken along the line II-II of the retardation substrate shown in FIG. 1.

The retardation substrate 10 shown in FIGS. 1 and 2 includes a substrate 110, a color filter layer 120 and a solidified liquid crystal layer 130.

The substrate 110 has a light-transmitting property. The substrate 110 is, for example, a transparent substrate.

The color filter layer 120 is formed on the substrate 110. The color filter layer 120 includes coloring layers 120 a to 120 c different in absorption spectrum from one another and adjacent to one another on the substrate 110. For example, the light transmitted by the coloring layer 120 a is longer in center wavelength than the light transmitted by the coloring layer 120 b, and the light transmitted by the coloring layer 120 b is longer in center wavelength than the light transmitted by the coloring layer 120 c. Note that the “center wavelength” of a certain light is the wavelength at which the spectrum of the particular light exhibits the maximum intensity.

The color filter layer 120 may further include one or more coloring layer different in absorption spectrum from the coloring layer 120 a to 120 c. Here, as an example, it is supposed that the first coloring layer 120 a is a red coloring layer, the second coloring layer 120 b is a green coloring layer, and the third coloring layer 120 c is a blue coloring layer.

Each of the coloring layers 120 a to 120 c has a band-like shape extending in the Y direction. The coloring layers 120 a to 120 c are alternately arranged in the X direction crossing the Y direction to form a stripe arrangement. Note that the X direction and the Y direction are directions parallel with the surface of the substrate 110 that face the color filter layer 120. Note also that the Z direction to be referred later is a direction perpendicular to the X direction and the Y direction.

The coloring layers 120 a to 120 c may have other shapes. For example, each of the coloring layers 120 a to 120 c has a rectangular shape. In this case, the coloring layers 120 a to 120 c may form a square arrangement of a delta arrangement.

Each of the coloring layers 120 a to 120 c is made of, for example, a mixture containing a transparent resin and a pigment dispersed therein. Forming a patterned layer of a coloring composition that contains a pigment and a pigment carrier and curing the patterned layer can obtain each of the coloring layers 120 a to 120 c. The coloring composition will be described later.

The solidified liquid crystal layer 130 is a retardation layer. The solidified liquid crystal layer 130 is formed on the color filter layer 120. Typically, the solidified liquid crystal layer is a continuous layer and covers the entire main surface of the color filter layer 120.

The solidified liquid crystal layer 130 and the color filter layer 120 may be in contact with each other or not. In the latter case, an alignment layer may be interposed between the solidified liquid crystal layer 130 and the color filter layer 120.

The solidified liquid crystal layer 130 includes three or more regions arranged in a direction parallel with the main surface thereof. At least two of the regions have form birefringence and cause different retardations.

Specifically, the solidified liquid crystal layer 130 includes regions 130 a to 130 d. The regions 130 a to 130 b are adjacent to one another in a direction perpendicular to the Z direction.

The regions 130 a to 130 c face the coloring layer 120 a to 120 c, respectively. The regions 130 a to 130 c have almost the same shape.

The regions 130 a to 130 c are smaller than the coloring layer 120 a to 130 b, respectively. The regions 130 a to 130 c are spaced apart from one another.

The region 130 d is the region of the solidified liquid crystal layer 130 other than the regions 130 a to 130 c. The region 130 d may be omitted. In this case, for example, the regions 130 a to 130 c is so arranged that their contours have almost the same positions as the contours of the coloring layers 120 a to 120 c, respectively.

The regions 130 a to 130 d are formed by polymerization and/or crosslinking of a thermotropic liquid crystal compound or composition. The regions 130 a to 130 d are equal in composition.

Typically, the regions 130 a to 130 d are equal in thickness. That is, typically, the solidified liquid crystal layer 130 has a uniform thickness.

The regions 130 a to 130 c are different in degree of orientation. The region 130 a is higher in degree of orientation than the region 130 b. The region 130 b is higher in degree of orientation than the region 130 c. Therefore, the region 130 a is greater in refractive index anisotropy than the region 130 b, and the region 130 b is greater in refractive index anisotropy than the region 130 c. Note that the region 130 c may have form birefringence or be optically isotropic.

Here, the “degree of orientation” refers to the degree of orientation of the mesogens MS in each of the regions adjacent in the in-plane direction. The degree of orientation of the mesogens MS may be uniform in the entire region or varied along the Z direction. For example, the degree of orientation may be higher near the lower surface and lower near the upper surface. In this case, the “degree of orientation” refers to an average of the degree of orientation in the direction of thickness.

A higher degree of orientation in the region 130 a than that in the region 130 b can be confirmed by comparing the refractive index anisotropy of the region 130 a with the refractive index anisotropy of the region 130 b. Similarly, a higher degree of orientation in the region 130 b than that in the region 130 c can be confirmed by comparing the refractive index anisotropy of the region 130 b with the refractive index anisotropy of the region 130 c.

As above, the regions 130 a to 130 c are different in degree of orientation. Further, the regions 130 a to 130 c are almost equal in thickness. Therefore, the regions 130 a to 130 c cause different retardations.

In the case where the mesogens have rod-like shape, each of the regions 130 a to 130 c may be, for example, a positive A-plate corresponding to a homogeneous alignment in which the longitudinal directions of the mesogens are aligned in a direction almost perpendicular to the Z direction, a positive C-plate corresponding to a homogeneous alignment in which the longitudinal directions of the mesogens are aligned in a direction almost parallel with the Z direction, or a negative C-plate that corresponds to a cholesteric alignment in which the mesogens form a helical structure having a helical axis almost parallel with the Z direction and the longitudinal directions of the mesogens are aligned in a direction almost perpendicular to the Z direction in each plane perpendicular to the helical axis. Also, in the case where the mesogens have rod-like shape, each of the regions 130 a to 130 c may be a composite of the positive A-plate and the negative C-plate corresponding to a cholesteric alignment deformed such that the longitudinal directions of the mesogens biased in a direction perpendicular to the Z direction. In the case where the mesogens have disk-like shape, each of the regions 130 a to 130 c is, for example, a negative A-plate corresponding a homeotropic alignment in which the thickness directions of the mesogens are aligned in a direction almost parallel with the Z direction, or a positive C-plate corresponding to a homogeneous alignment in which the thickness directions of the mesogens are aligned in a direction almost perpendicular to the Z direction. As above, the regions 130 a to 130 c may employ any alignment structure.

As mentioned above, the region 130 c may be optically isotropic. That is, in the region 130 c, it is unnecessary that the mesogens form an alignment structure.

As described above, the retardation substrate 10 includes regions 130 a to 130 c different in refractive index anisotropy from one another. For this reason, it is unnecessary to make the thicknesses of the regions 130 a to 130 c different from one another in order to make the retardations caused thereby different from one another. Thus, although the thicknesses of the regions 130 a to 130 c may be different from one another, the thicknesses of the regions 130 a to 130 c can be made equal to one another. Therefore, the solidified liquid crystal layer 130 can be manufactured easily.

Further, the solidified liquid crystal layer 130 as a continuous film makes the mass transfer from the color filter layer 120 to the outside of the retardation substrate 10 more difficult than a patterned solidified liquid crystal layer 130. Therefore, in the case where the retardation substrate 10 that includes the solidified liquid crystal layer 130 as a continuous layer is used, for example, in a liquid crystal layer, it is possible to suppress the inclusion of impurities from the color filter layer 120 into the liquid crystal layer.

Next, materials and manufacturing methods of the retardation substrate 10 will be described.

The substrate 10 is, typically, a light-transmitting substrate such as glass plate or resin plate. As a material of the glass plate, soda-lime glass, low-alkali borosilicate glass or non-alkali amino borosilicate glass can be used, for example. As a material of the resin plate, polycarbonate, polymethyl methacrylate or polyethylene terephthalate may be used, for example.

The substrate 10 may have a monolayer structure or a multi-layered structure. For example, in the case where the retardation substrate 10 is a component of a liquid crystal display, a light-transmitting substrate on which a transparent electrode made of transparent conductor such as indium tin oxide or tin oxide may be used as the substrate 10. Alternatively, as the substrate 110, a light-transmitting substrate on which a circuit such as pixel circuit is formed may be used.

The substrate 110 may be a light-transmitting film such as plastic film or a light-transmitting sheet such as plastic sheet.

It is unnecessary that the substrate 110 has a light-transmitting property. For example, when the retardation substrate employs the structure in which reflected light is utilized instead of transmitted light, the substrate 110 may have light-shielding property.

For forming the color filter layer 120, any method may be employed. According to an example, each of the coloring layers 120 a to 120 c can be obtained by forming a film of a coloring composition that contains a pigment carrier and a pigment dispersed therein and curing the film.

As the pigment of the coloring composition, organic pigment and/or inorganic pigment can be used. The coloring composition may contain a single organic or inorganic pigment, or a plurality of organic pigments and/or inorganic pigments.

A pigment excellent in coloring property and heat-resisting property, in particular, thermal decomposition-resisting property is preferable, and normally, organic pigments are utilized. The following color index numbers are examples of the organic pigments that can be used in the coloring composition.

As an organic pigment of a red coloring composition, a red pigment such as C. I. Pigment Red 7, 14, 41, 48:2, 48:3, 48:4, 81:1, 81:2, 81:3, 81:4, 146, 168, 177, 178, 179, 184, 185, 187, 200, 202, 208, 210, 246, 254, 255, 264, 270, 272 or 279 can be used, for example. As an organic pigment of a red coloring composition, a mixture of a red pigment and a yellow pigment may be used. As the yellow pigment, C. I. Pigment Yellow 1, 2, 3, 4, 5, 6, 10, 12, 13, 14, 15, 16, 17, 18, 24, 31, 32, 34, 35, 35:1, 36, 36:1, 37, 37:1, 40, 42, 43, 53, 55, 60, 61, 62, 63, 65, 73, 74, 77, 81, 83, 93, 94, 95, 97, 98, 100, 101, 104, 106, 108, 109, 110, 113, 114, 115, 116, 117, 118, 119, 120, 123, 126, 127, 128, 129, 138, 147, 150, 151, 152, 153, 154, 155, 156, 161, 162, 164, 166, 167, 168, 169, 170, 171, 172, 173, 174, 175, 176, 177, 179, 180, 181, 182, 185, 187, 188, 193, 194, 199, 198, 213 or 214 can be used, for example.

As an organic pigment of a green coloring composition, a green pigment such as C. I. Pigment Green 7, 10, 36 or 37 can be used, for example. As an organic pigment of a green coloring composition, a mixture of a green pigment and a yellow pigment may be used. As the yellow pigment, the same pigments as that described for the red coloring composition can be used, for example.

As an organic pigment of a blue coloring composition, a blue pigment such as C. I. Pigment Blue 15, 15:1, 15:2, 15:3, 15:4, 15:6, 16, 22, 60 or 64 can be used, for example. As an organic pigment of a blue coloring composition, a mixture of a blue pigment and a purple pigment may be used. As the purple pigment, C. I. Pigment Violet 1, 19, 23, 27, 29, 30, 32, 37, 40, 42 or 50 can be used, for example.

As the inorganic pigment, metal oxide powders, metal sulfide powders, or metal powders such as yellow lead ore, zinc yellow, iron red (red oxide of iron (III)), cadmium red, ultramarine blue, chromic oxide green and cobalt green can be used, for example. The inorganic pigment can be used, for example, in combination with the organic pigment in order to achieve excellent application property, sensitivity and developing property while balancing chroma and lightness.

The coloring composition may further contain coloring components other than the pigment. For example, the coloring composition may contain dye if a sufficient thermal resistance can be achieved. In this case, the dye can be used for color matching.

The transparent resin is a resin having a transmittance of preferably 80% or higher, more preferably 95% or higher throughout the entire wavelength range of 400 to 700 nm, which is the visible range. As the material of the transparent resin, i.e., the pigment carrier, transparent resins such as thermoplastic resin, thermosetting resin and photosensitive resin, the precursors thereof, or the mixture thereof can be used, for example. The transparent resin as the pigment carrier is, for example, a thermoplastic resin, a thermosetting resin a photosensitive resin or a mixture containing two or more of them. The precursor of the transparent resin is, for example, monomers and/or oligomers that cure when irradiated with rays.

In the coloring composition, the transparent resin is use at an amount of, for example, 30 to 700 parts by mass, preferably 60 to 450 parts by mass with respect to 100 parts by mass of the pigment. In the case where a mixture of the transparent resin and the precursor thereof is used as the pigment carrier, the transparent resin is used in the coloring composition at an amount of, for example, 20 to 400 parts by mass, preferably 50 to 250 parts by mass with respect to 100 parts by mass of the pigment. In this case, the precursor of the transparent resin is used in the coloring composition at an amount of, for example, 10 to 300 parts by mass, preferably 10 to 200 parts by mass with respect to 100 parts by mass of the pigment.

As the thermoplastic resin, butyral resins, styrene-maleic acid copolymers, chlorinated polyethylenes, polyvinyl chlorides, vinyl chloride-vinyl acetate copolymers, polyvinyl acetates, polyurethane resins, polyester resins, acrylic resins, alkyd resins, polystyrene resins, polyamide resins, rubber-based resins, cyclized rubber resins, celluloses, polybutadiens, polyethylenes, polypropylenes or polyimide resins can be used, for example.

As the thermosetting resin, epoxy resins, benzoguanamine resins, rosin-modified maleic resins, melamine resins, urea resins or phenol resins can be used, for example.

As the photosensitive resin, resins obtained by causing the reaction of an acrylic compound, a methacrylic compound or cinnamic acid having a reactive substituent such as isocyanate group, aldehyde group and epoxy group with a linear polymer having a reactive substituent such as hydroxyl group, carboxyl group and amino group to introduce photo-crosslinking groups such as acryloyl groups, methacryloyl groups and stylyl groups into the linear polymer can be used, for example. Alternatively, resins obtained by half-esterifying a linear polymer including acid anhydride such as styrene-maleic anhydride copolymer and α-olefin-maleic anhydride copolymer using acrylic compounds or methacrylic compounds having hydroxyl group such as hydroxyalkyl acrylates and hydroxyalkyl methacrylates may be used.

As the monomers and/or oligomers, which are the precursor of the transparent resin, acrylic esters and methacrylic esters such as 2-hydroxyethyl acrylate, 2-hydroxyetyl methacrylate, 2-hydroxypropyl acrylate, 2-hydroxypropyl methacrylate, cycrohexyl acrylate, cycrohexyl methacrylate, polyethylene glycol diacrylate, polyethylene glycol dimethacrylate, pentaerythritol triacrylate, pentaerythritol trimethacrylate, trimethylolpropane triacrylate, trimethylolpropane trimethacrylate, dipentaerythritol hexaacrylate, dipentaerythritol hexamethacrylate, tricyclodecanyl acrylate, tricyclodecanyl methacrylate, melamine acrylate, melamine methacrylate, epoxy acrylate and epoxy methacrylate; acrylic acid, methacrylic acid, styrene, vinyl acetate, acrylamide, methacrylamide, N-hydroxymethyl acrylamide, N-hydroxymethyl methacrylamide or a mixture containing two or more of them can be used, for example.

In the case where the coloring composition is cured using light such as ultraviolet rays, for example, a photo-polymerization initiator is added to the coloring composition.

As the photo-polymerization initiator, acetophenone-based photo-polymerization initiator such as 4-phenoxydichloroacetophenone, 4-t-butyl-dichloroacetophenone, diethoxyacetophenone, 1-(4-isopropylphenyl)-2-hydroxy-2-methylpropane-1-one, 1-hydroxycyclohexylphenylketone, 2-methyl-1[4-(methylthio)phenyl]-2-morpholinopropane-1-one and 2-benzyl-2-dimethylamino-1-(4-morpholinophenyl)-butane-1-one; benzoin-based photo-polymerization initiator such benzoin, benzoylbenzoate, methylbenzoylbenzoate, 4-phenylbenzophenone, hydroxybenzophenone, acrylated benzophenone and 4-benzoyl-4′-methyldiphenyl sulfide; thioxanthone-based photo-polymerization initiator such as thioxanthone, 2-chlorothioxanthone, 2-methyltioxanthone, isopropylthioxanthone and 2,4-diisopropylthioxanthone; triazine-based photo-polymerization initiator such as 2,4,6-trichloro-s-triazine, 2-phenyl-4,6-bis(trichloromethyl)-s-triazine, 2-(p-methoxyphenyl)-4,6-bis(trichloromethyl)-s-triazine, 2-(p-tolyl)-4,6-bis(trichloromethyl)-s-triazine, 2-piperonyl-4,6-bis(trichloromethyl)-s-triazine, 2,4-bis(trichloromethyl)-6-styryl-s-triaine, 2-(naphto-1-yl)-4,6-bis(trichloromethyl)-s-triazine, 2-(4-methoxy-naphto-1-yl)-4,6-bis(trichloromethyl)-s-triazine, 2,4-trichloromethyl-(piperonyl)-6-triazine and 2,4-trichloromethyl(4′-methoxystyryl)-6-triazine; borate-based photo-polymerization initiator; carbazole-based photo-polymerization initiator; imidazole-based photo-polymerization initiator; or a mixture containing two or more of them can be used, for example.

The photo-polymerization initiator is used in the coloring composition at an amount of, for example, 5 to 200 parts by mass, preferably 10 to 150 parts by mass with respect to 100 parts by mass of the pigment.

A sensitizer may be used together with the photo-polymerization initiator.

As the sensitizer, a compound such as α-acyloxy ester, acylphosphine oxide, methylphenyl glyoxylate, benzil, 9,10-phenanthrenequinone, camphor quinone, ethyl anthraquinone, 4,4′-diethyl isophthaloquinone, 3,3′,4,4′-tetra(t-butylperoxycarbonyl)benzophenone and 4,4′-diehylamino benzophenone can be used.

The sensitizer is used at an amount of, for example, 0.1 to 60 parts by mass with respect to 100 parts by mass of the photo-polymerization initiator.

The coloring composition may further contain a chain transfer agent such as multi-functional thiol.

A multi-functional thiol is a compound having two or more thiol groups. As the multi-functional thiol, hexanedithiol, decanedithiol, 1,4-butanediol bisthiopropionate, 1,4-butanediol bisthioglycolate, ethylene glycol bisthioglycolate, ethylene glycol bisthiopropionate, trimethylolpropane tristhioglycolate, trimethylolpropane tristhiopropionate, trimethylolpropane tris(3-mercaptobutyrate), pentaerythritol tetrakisthioglycolate, pentaerythritol tetrakisthiopropionate, trimercaptopropionic tris(2-hydroxyethyl)isocyanurate, 1,4-dimethylmercaptobenzene, 2,4,6-trimercapto-s-triazine, 2-(N,N-dibutylamino)-4,6-dimercapto-s-triazine or a mixture containing two or more of them can be used, for example.

The multi-functional thiol is used in the coloring composition at an amount of, for example, 0.2 to 150 parts by mass, preferably 0.2 to 100 parts by mass with respect to 100 parts by mass of the pigment.

The coloring composition may further contain a solvent. When the solvent is used, the dispersibility of the pigment increases. As a result, the coloring composition can be easily applied to the substrate 110 at a dried thickness of, for example, 0.2 to 5 μm.

As the solvent, cyclohexanone, ethyl cellosolve acetate, butyl cellosolve acetate, 1-methoxy-2-propyl acetate, diethylene glycol dimethoxy ether, ethyl benzene, ethylene glycol diethyl ether, xylene, ethyl cellosolve, methyl-n amyl ketone, propylene glycol monomethyl ether, toluene, methyl ethyl ketone, ethyl acetate, methanol, ethanol, isopropyl alcohol, butanol, isobutyl ketone, petroleum solvent, or a mixture containing two or more of them can be used, for example.

The solvent is used in the coloring composition at an amount of, for example, 800 to 4,000 parts by mass, preferably 1,000 to 2,500 parts by mass with respect to 100 parts by mass of the pigment.

The coloring composition can be manufactured, for example, by finely dispersing one or more pigment into the pigment carrier and the organic solvent together with the above-described photo-polymerization initiator as needed using a dispersing device such as three-roll mill, two-roll mill, sand mill, kneader and attritor. A coloring composition containing two or more pigments may be manufactured by preparing dispersions containing different pigments and mixing the dispersions together.

When dispersing the pigment into the pigment carrier and the solvent, a dispersion aid such as resin-type pigment-dispersing agent, surfactant and pigment derivative may be used. The dispersion aid increases the dispersibility of the pigment and suppresses the reaggregation of the dispersed pigment. Therefore, in the case of using a coloring composition prepared by dispersing a pigment into a pigment carrier and a solvent using a dispersion aid, a color filter excellent in transparency can be obtained.

The dispersion aid is used in the coloring composition at an amount of, for example, 0.1 to 40 parts by mass, preferably 0.1 to 30 parts by mass with respect to 100 parts by mass of the pigment.

The resin-type pigment-dispersing agent includes a pigment-affinitive moiety having a property of undergoing adsorption by the pigment and a moiety having a compatibility with the pigment carrier. The resin-type pigment-dispersing agent is adsorbed by the pigment so as to stabilize the dispersibility of the pigment in the pigment carrier.

As the resin-type pigment-dispersing agent, an oil-based dispersing agent such as polyurethane, polycarboxylate, e.g. polyacrylate, unsaturated polyamide, polycarboxylic acid, partial amine salt of polycarboxylic acid, ammonium polycarboxylate, alkylamine polycarboxylate, polysiloxane, long-chain polyaminoamide phosphate and hydroxyl group-containing polycarboxylate, modified compounds thereof, amide produced through a reaction of poly(lower alkylene imine) with polyester having a free carboxyl group and a salt thereof; water-soluble resin or water-soluble macromolecular compound such as acrylic acid-styrene copolymer, methacrylic acid-styrene copolymer, acrylic acid-acrylate copolymer, acrylic acid-methacrylate copolymer, methacrylic acid-acrylate copolymer, methacrylic acid-methacrylate copolymer, styrene-maleic acid copolymer, polyvinyl alcohol and polyvinyl pyrrolidone; polyester; modified polyacrylate; ethylene oxide/propylene oxide adduct; phosphate; or a compound containing two or more of them can be used, for example.

As the surfactant, an anionic surfactant such as polyoxyethylene alkylether sulfate, dodecylbenzene sodium sulfonate, alkali salt of styrene-acrylic acid copolymer, alkylnaphthaline sodium sulfonate, alkyldiphenyl ether sodium disulfonate, monoethanol amine lauryl sulfate, triethanol amine lauryl sulfate, ammonium lauryl sulfate, monoethanol amine stearate, sodium stearate, sodium lauryl sulfate, monoethanol amine of styrene-acrylic acid copolymer and polyoxyethylene alkylether phosphate; a nonionic surfactant such as polyoxyethylene oleyl ether, polyoxyethylene lauryl ether, polyoxyethylene nonylphenyl ether, polyoxyethylene alkylether phosphate, polyoxyethylene sorbitan monostearate and polyethyleneglycol monolaurate; a cationic surfactant such as alkyl quaternary ammonium salt and an ethylene oxide adduct thereof; an amphoteric surfactant such as alkyl betaine, e.g. betaine alkyldimethyl aminoacetate and alkylimidazoline; and a mixture containing two or more of them can be used, for example.

The dye derivative is a compound produced by introducing a substituent into an organic dye. Although the dye derivative is similar in hue to the pigment used, the hue of the former may be different from that of the latter if the loading thereof is small. Note that the term “organic dye” includes aromatic polycyclic compounds exhibiting a light yellow color such as naphthalene-based compounds and anthraquinone-based compounds, which are generally not referred to as “dye”, in addition to compounds generally referred to as “dye”. As the dye derivative, those described in JP-A 63-305173, JP-B 57-15620, JP-B 59-40172, JP-B 63-17102 or JP-B 5-9469 can be used, for example. Especially, the dye derivatives having a basic group are highly effective in the dispersion of pigment. The coloring composition may contain a single dye derivative or a plurality of dye derivatives.

A storage-stability improver may be added to the coloring composition in order to improve the temporal stability of its viscosity. As the storage-stability improver, benzyltrimethyl chloride; quaternary ammonium chloride such as diethylhydroxy amine; organic acid such as lactic acid and oxalic acid; methyl ether of the organic acid; t-butyl pyrocatechol; organic phosphine such as tetraethyl phosphine and tetraphenyl phosphine; phosphite; or a mixture containing two or more of them can be used, for example.

The storage-stability improver is contained in the coloring composition at an amount of, for example, 0.1 to 10 parts by mass with respect to 100 parts by mass of the pigment.

To the coloring composition, an adhesion improver such as silane coupling agent may be added in order to improve the adhesion to the substrate.

As the silane coupling agent, vinyl silane such as vinyl tris(β-methoxyethoxy)silane, vinylethoxy silane and vinyltrimethoxy silane; acrylsilane and metacrylsilane such as γ-methacryloxypropyl trimethoxy silane; epoxy silane such as β-(3,4-epoxycyclohexyl)ethyltrimethoxy silane, β-(3,4-epoxycyclohexyl)methyltrimethoxy silane, β-(3,4-epoxycyclohexyl)ethyltriethoxy silane, β-(3,4-epoxycyclohexyl)methyltriethoxy silane, γ-glycidoxypropyl trimethoxy silane and γ-glycidoxypropyl triethoxy silane; amino silane such as N-β(aminoethyl) γ-aminopropyl trimethoxy silane, N-β(aminoethyl) γ-aminopropyl triethoxy silane, N-β(aminoethyl) γ-aminopropyl methyldiethoxy silane, γ-aminopropyl triethoxy silane, γ-aminopropyl trimethoxy silane, N-phenyl-γ-aminopropyl trimethoxy silane and N-phenyl-γ-aminopropyl triethoxy silane; thiosilane such as γ-mercaptopropyl trimethoxy silane and γ-mercaptopropyl triethoxy silane; or a mixture containing two or more of them can be used, for example.

The silane coupling agent is contained in the coloring composition at an amount of, for example, 0.01 to 100 parts by mass with respect to 100 parts by mass of the pigment.

The coloring composition can be prepared in the form of a gravure offset printing ink, a waterless offset printing ink, a silk screen printing ink, or a solvent developer-type or alkaline developer-type colored resist. The colored resist is the one that is obtained by dispersing dye in a composition containing a thermoplastic resin, thermosetting resin or photosensitive resin, a monomer, a photo-polymerization initiator and an organic solvent.

The pigment is used at an amount of, for example, 5 to 70 parts by mass, preferably 20 to 50 parts by mass with respect to 100 parts by mass of the total solid contents in the coloring composition. Note that most of the remainder of the solid contents in the coloring layer is the resin binder included in the pigment carrier.

Prior to using the coloring composition for forming a film, particles having a size of 5 μm or more, preferably 1 μm or more, more preferably 0.5 μm or more may be removed from the coloring composition using a refiner such as centrifugal separator, sintered filter and membrane filter.

Each of the coloring layers 120 a to 120 c can by formed, for example, by printing. According to printing, printing using the coloring composition and drying it thereafter can form each of the coloring layers 120 a to 120 c. Therefore, the printing method is low cost and excellent in mass productivity. Further, since the printing technique is improved in recent years, printing can form fine patterns having high dimension accuracy and high smoothness.

In the case where printing is used, the coloring composition should be designed to have a composition that would not cause the coloring composition to be dried and solidified on the printing plate or the blanket. Also, in the printing, it is important to optimize the flowability of the coloring composition in the printer. Therefore, a dispersing agent or an extender may be added to the coloring composition so as to adjust the viscosity thereof.

Each of the coloring layers 120 a to 120 c may be formed using photolithography. According to photolithography, the color filter layer 120 can be formed with higher accuracy as compared with the case where printing is utilized.

In this case, the coloring composition prepared as a solvent developer-type or alkaline developer-type colored resist is applied first to the substrate 110. For this application, an application method such as spray coating, spin coating, slit coating and roll coating is utilized. The coated film is formed to have a dried thickness of, for example, 0.2 to 10 μm.

Next, the coated film is dried. For example a vacuum drier, a convection oven, an IR oven or a hot plate is used for drying the coated film. Drying the coated film can be omitted.

Subsequently, the coated film is irradiated with ultraviolet rays via a photomask. That is, the coated film is subjected to a pattern exposure.

Then, the coated film is immersed in a solvent developer or an alkaline developer. Alternatively, the coated film is sprayed with the developer. Thus, soluble portions are removed from the coated film to obtain the coloring layer 120 a as a resist pattern.

Further, by the same method as described above, the coloring layers 120 b and 120 c are formed in this order. Thus, the color filter layer 120 is obtained. Note that in this method, a heat treatment may be executed in order to promote the polymerization of the colored resists.

In the photolithography process, for example, an aqueous solution of sodium carbonate or sodium hydroxide can be used as the alkaline developer. Alternatively, a liquid containing an organic alkali such as dimethylbenzyl amine and triethanol amine may be used as the alkaline developer.

An additive such as defoaming agent or surfactant may be added to the developer. A shower developing method, a spray developing method, a dip developing method or a paddle developing method may be utilized for developing, for example.

In order to enhance the sensitivity to light exposure, the following process may be further executed. That is, after drying the first coated film of the colored resist, an alkaline-soluble resin, for example, polyvinyl alcohol or water-soluble acrylic resin is applied to the first coated film. After drying the second coated film, the above-described pattern exposure is performed. The second coated film prevents the polymerization in the first coated film from being inhibited by oxygen. Therefore, a higher sensitivity to light exposure can be achieved.

The color filter layer 120 may be formed by other methods. For example, it may be formed using an inkjet method, an electrode position method or a transfer method. In the case where the color filter layer 120 is formed using the inkjet method, each coloring layer is obtained, for example, by forming a light-shielding partition wall on the substrate 110 in advance and injecting an ink from a nozzle toward regions separated by the light-shielding partition wall. In the case where the color filter layer 120 is formed using the electrode position method, each coloring layer is obtained, for example, by forming a transparent conductive layer on the substrate 110 in advance and depositing the coloring composition on the transparent conductive film utilizing an electrophoresis of colloidal particles made of the coloring composition. In the case where the transfer method is used, the color filter layer 120 is formed on a surface of a releasable transfer base sheet in advance, and then the color filter layer 120 is transferred from the base sheet onto the substrate 110.

Next, a method for manufacturing the solidified liquid crystal layer 130 will be described.

FIGS. 3 and 4 are sectional views schematically showing an example of a method of forming a solidified liquid crystal layer.

The solidified liquid crystal layer 130 is obtained, for example, by forming a liquid crystal material layer 130′ containing a photo-polymerizing or photo-crosslinking thermotropic liquid crystal material on the color filter layer 120 and subjecting the liquid crystal material layer 130′ to a pattern exposure and a heat treatment.

The liquid crystal material layer 130′ can be obtained, for example, by applying a coating solution containing a thermotropic liquid crystal compound on the color filter layer 120 and drying the coated film, if necessary. In the liquid crystal material layer 130′, the mesogens of the thermotropic liquid crystal compound form an alignment structure.

In addition to the thermotropic liquid crystal compound, components such as solvent, chiral agent, photo-polymerization initiator, thermal polymerization initiator, sensitizer, chain transfer agent, multi-functional monomer and/or oligomer, resin, surfactant, storage-stability improver and adhesion improver can be added to the coating solution to the extent that the composition containing the liquid crystal compound does not lose mesomorphism.

As the thermotropic liquid crystal compound, alkyl cyanobiphenyl, alkoxy biphenyl, alkyl terphenyl, phenyl cyclohexane, biphenyl cyclohexane, phenyl bicyclohexane, pyrimidine, cyclohexane carboxylic acid ester, halogenated cyanophenol ester, alkyl benzoic acid ester, alkyl cyanotolane, dialkoxy tolane, alkyl alkoxy tolane, alkyl cyclohexyl tolane, alkyl bicyclohexane, cyclohexyl phenyl ethylene, alkyl cyclohexyl cyclohexene, alkyl benzaldehyde azine, alkenyl benzaldehyde azine, phenyl naphthalene, phenyl tetrahydronaphtalene, phenyl decahydronaphthalene, derivatives thereof, or acrylates of the compounds can be used, for example.

As the photo-polymerization initiator, sensitizer, chain transfer agent, multi-functional monomer and/or oligomer, resin, surfactant, storage-stability improver and adhesion improver, the same materials as that exemplified for the coloring composition can be used, for example. Also, as the solvent, the same materials as that exemplified for the coloring composition can be used, for example.

For applying the coating solution, a printing method such as spin coating, slit coating, relief printing, screen printing, planographic printing, reverse printing and gravure printing; the printing method incorporated into an offset system; an inkjet method; or bar coat method can be used, for example.

The liquid crystal material layer 130′ is formed, for example, as a continuous layer having a uniform thickness. According to the method described above, the liquid crystal material layer 130′ can be formed as a continuous film having a uniform thickness as long as the surface to be coated is sufficiently flat.

Prior to the application of the coating solution, the surface of the color filter layer 120 may be subjected to an alignment process such as rubbing process. Alternatively, prior to the application of the coating solution, an alignment layer for regulating the orientation of the liquid crystal compound may be formed on the color filter layer 120. Forming a transparent layer of resin such as polyimide on the color filter layer 120 and subjecting the transparent resin layer to an alignment process such as rubbing process can obtain the alignment layer, for example. The alignment layer may be formed using a photo-alignment technique.

Then, a first exposure process is performed. That is, as shown in FIG. 3, regions of the liquid crystal material layer 130′ are irradiated with light L1 at different exposure values. For example, the region 130 a′ of the liquid crystal material layer 130′ that corresponds to the region 130 a is irradiated with the light L1 at the maximum exposure value. The region 130 b′ of the liquid crystal material layer 130′ that corresponds to the region 130 b is irradiated with the light L1 at an exposure value lower than that for the region 130 a′. The region 130 c′ of the liquid crystal material layer 130′ that corresponds to the region 130 c is irradiated with the light L1 at an exposure value lower than that for the region 130 b′ or not irradiated with the light L1. Thus, at the portions of the liquid crystal material layer 130′ that are irradiated with the light L1, the thermotropic liquid crystal compound polymerizes or forms crosslinks while maintaining the alignment structure of the mesogens. In the polymerized or crosslinked product of the thermotropic liquid crystal compound, the mesogenic groups are immobilized.

The region 130 a′ irradiated with light at the maximum exposure value is the highest in the content of the polymerized or crosslinked product of the thermotropic liquid crystal compound and the lowest in the unpolymerized or uncrosslinked thermotropic liquid crystal compound. The region 130 b′ irradiated with light at the exposure value lower than that for the region 130 a′ is lower in the content of the polymerized or crosslinked product of the thermotropic liquid crystal compound and higher in the content of the unpolymerized or uncrosslinked thermotropic liquid crystal compound than the region 130 a′. The region 130 c′ irradiated with light at the exposure value lower than that for the region 130 b′ is lower in the content of the polymerized or crosslinked product of the thermotropic liquid crystal compound and higher in the content of the unpolymerized or uncrosslinked thermotropic liquid crystal compound than the region 130 b′. For example, the whole thermotropic liquid crystal compound in the region 130 a′ is polymerized or crosslinked, only a part of the liquid crystal compound in the region 130 b′ is polymerized or crosslinked, and almost no thermotropic liquid crystal compound in the region 130 c′ is polymerized or crosslinked.

The light L1 used in the first exposure process is electromagnetic waves such as ultraviolet rays, visible rays and infrared rays. An electron beam may be used instead of the electromagnetic waves. Only one of them may be used as the light L1. Alternatively, two or more of them may be used as the light L1.

The first exposure process may be performed by any method as long as the above-described nonuniform polymerization or crosslinking can be caused.

For example, the exposure process may include an exposure using a certain photomask and another exposure using a photomask different in a pattern of a light-shielding layer from the former. In this case, the whole liquid crystal material layer 130′ is irradiated with the light L1, then, only the regions 130 a′ and 130 b′ are irradiated with the light L1 using a certain photomask, and finally, only the region 130 a is irradiated with the light L1 using another photomask, for example.

Alternatively, the exposure process may include an exposure for the region 130 a′ using a certain photomask, another exposure for the region 130 b′ using the same photomask, and an optional exposure for the region 130 c′ using the same photomask. In this case, the region 130 a′ is irradiated with the light L1 at the maximum exposure value using a certain photomask, the region 130 b′ is irradiated with the light L1 at an exposure value lower than that for the region 130 a′ using this photomask, and the region 130 c′ is irradiated with the light L1 at an exposure value lower than that for the region 130 b′ using the same photomask, for example.

Alternatively, the exposure process may include an exposure using a halftone mask. For example, the liquid crystal material layer 130′ is irradiated with the light through a halftone mask provided with a light-shielding layer and a semitransparent layer at positions corresponding to the regions 130 c′ and 130 c′, respectively. Instead of the halftone mask, a gray-tone mask or a wavelength-limiting mask may be used. The gray-tone mask has the same structure as that of the halftone mask except that the semitransparent layer is omitted and it further includes at a position corresponding to the region 130 b′ a light-shielding layer, which is provide with slits each having a width equal to or smaller than the resolution of the light-exposure apparatus. The light-limiting mask includes portions different in wavelength range of light allowed to pass through.

Alternatively, the liquid crystal material layer 130′ may be scanned with rays or luminous flux such as electron beam instead of using a photomask.

Alternatively, the above-described techniques may be combined together.

After completing the first exposure process, a first heat treatment process is performed. That is, the liquid crystal material layer 130′ is heated to a temperature equal to or higher than the phase transition temperature at which the thermotropic liquid crystal compound changes from a liquid crystal phase to an isotropic phase. The mesogens of the thermotropic liquid crystal compound as an unreacted compound are not immobilized. Therefore, when the liquid crystal material layer 130′ is heated to the phase transition temperature or higher, the degree of orientation of the mesogens is lowered. For example, the mesogens of the unreacted compound changes from the liquid crystal phase to the isotropic phase. On the other hand, the mesogens of the polymerized or crosslinked product of the thermotropic liquid crystal compound are immobilized.

Therefore, as shown in FIG. 4, the degree of orientation of the mesogens MS in the region 130 b′ becomes lower than that in the region 130 a′. Also, the degree of orientation of the mesogens MS in the region 130 c′ becomes lower than that in the region 130 b′. For example, the heat treatment causes in the region 130 a′ almost no change in the degree of orientation of the mesogens MS. The heat treatment degreases the degree of orientation of the mesogens MS decreases in the region 130 b′. And, the heat treatment destroys the alignment structure of the mesogens MS in the region 130 c′.

Then, the unreacted compound is polymerized and/or crosslinked while the degree of orientation of the mesogens of the unreacted compound kept lowered.

For example, the second exposure process shown in FIG. 4 is performed. That is, the entire liquid crystal compound layer 130′ is irradiated with light L2 while keeping the temperature of the liquid crystal compound layer 130′ higher than the phase transition temperature at which the thermotropic liquid crystal compound changes from the isotropic phase to the liquid crystal phase. The liquid crystal compound layer 130′ is irradiated with the light L2 at an exposure value sufficient for almost the whole unreacted compound to cause the polymerization and/or crosslinking reaction. Thus, the unreacted compound is polymerized or crosslinked to immobilize the mesogens whose degree of orientation has been lowered. As above, the solidified liquid crystal layer 130 is obtained.

Note that a first phase transition temperature of some liquid crystal compounds at which an isotropic phase changes to a liquid crystal phase is lower than a second phase transition temperature at which the liquid crystal phase changes to the isotropic phase. Therefore, in particular cases, the temperature of the liquid crystal compound layer 130′ in the second exposure process may be lower than the heating temperature in the first heat treatment process. However, in ordinary cases, the temperature of the liquid crystal compound layer 130′ in the second exposure process is set at the first phase transition temperature or higher in terms of convenient.

As the light L2, the same light as that described for the light L1 can be used. The light L2 and the light L1 may be the same or not.

In the second exposure process, the exposure value may be uniform throughout the entire liquid crystal compound layer 130′. In this case, it is unnecessary to use a photomask provide with a fine pattern. Therefore, in this case, the process can be simplified.

Alternatively, the second exposure process may be performed such that the regions 130 a′ to 130 c′ are equal in total exposure value, which is a sum of exposure values in the first and second exposure processes, to one another. For example, in the case where the total exposure value of the region 130 a′ is remarkably higher than the total exposure value of the region 130 c′, it is possible that the region 130 a′ and/or the coloring layer 120 a are damaged undesirably. When the total exposure values of the region 130 a′ to 130 c′ are equal to one another, such damage can be prevented.

The polymerization and/or crosslinking of the unreacted compound can be performed by other methods.

For example, in the case where the unreacted compound, i.e., the thermotropic liquid crystal compound is a substance that polymerizes and/or forms crosslinks when heated to a polymerization and/or crosslinking temperature higher than the first phase transition temperature, a second heat treatment process may be performed instead of the second exposure process. Specifically, instead of the second exposure process, the liquid crystal material layer 130 is heated to the polymerization and/or crosslinking temperature or higher to cause the polymerization and/or crosslinking of the unreacted compound. Thus, the solidified liquid crystal layer 130 is obtained. Note that the heating temperature in the first heat treatment is set, for example, equal to or higher than the first phase transition temperature and lower than the polymerization and/or crosslinking temperature.

Alternatively, the second heat treatment process and the second exposure process may be performed in this order after the first heat treatment process. Alternatively, the second exposure process and the second heat treatment process may be performed in this order after the first heat treatment process. Alternatively, the second heat treatment process, the second exposure process and the second heat treatment process may be performed in this order after the first heat treatment process. When the second exposure process and the second heat treatment process are combined together as above, the polymerization and/or crosslinking of the unreacted compound can proceed with a higher degree of reliability. Therefore, a stronger solidified liquid crystal layer 130 can be obtained.

In the case where the unreacted compound is the substance that polymerizes and/or forms crosslinks when heated to a certain temperature, the heating temperature in the first heat treatment may be equal to or higher than the temperature at which it polymerizes and/or forms crosslinks. However, in this case, the decrease in the degree of orientation and the polymerization and/or crosslinking proceed simultaneously. For this reason, the influence of the manufacturing conditions on the optical properties of the solidified liquid crystal layer is comparatively large.

Meanwhile, in the case where a developing process is performed after the first exposure process, obtained is the solidified liquid crystal layer that includes regions equal in refractive index anisotropy to each other and different in thickness from each other. The regions cause different retardations because they are different in thickness from each other.

However, conditions of a wet process, in particular, a development is difficult to control precisely, and these conditions greatly affect the optical properties of the final product. For this reason, according to the method including a wet process, deviations of the optical properties from the target values prone to occur.

In contrast, according to the method described with reference to FIGS. 3 and 4, no wet process is performed in the first exposure process or later. Therefore, according to this method, it is possible to prevent the deviation of the refractive index anisotropy from the target value due to the wet process.

Note that the refractive index anisotropy and the exposure value in the first exposure process are not always in a proportional relation. However, under the conditions in which materials and the exposure values are unchanged, the reproducibility of the refractive index anisotropy is high. Therefore, the conditions, for example, an exposure value necessary for achieving certain refractive index anisotropy can be found out easily, and a stable manufacture can be done easily.

Various modifications can be made to the retardation substrate 10 described with reference to FIGS. 1 to 4, i.e., a panel substrate.

In the retardation substrate 10, the solidified liquid crystal layer 130 includes the regions 130 a to 130 c different in refractive index anisotropy. The solidified liquid crystal layer 130 may further include one or more regions different in refractive index anisotropy from the regions 130 a to 130 c. For example, in a semi-transparent liquid crystal display, each of the red, green and blue pixels includes a transmissive portion and a reflective portion. The transmissive portion and the reflective portion need to be designed separately. Therefore, each of the portions of the solidified liquid crystal layer 130 that correspond to the red, green and blue pixels may include two or more regions different in refractive index anisotropy from each other.

The color filter layer 120 may be omitted from the retardation substrate 10. For example, in a liquid crystal display, one of the substrates may include both a color filter layer and a retardation layer. Alternatively, it is possible that one substrate of a liquid crystal display includes a color filter layer and the other substrate includes a retardation layer. In the latter case, it is not necessary that the retardation substrate 10 includes the color filter layer 120. However, in the case where the retardation substrate 10 includes both the color filter layer 120 and the solidified liquid crystal layer 130, an alignment between the color filter layer 120 and the solidified is unnecessary when bonding them together.

The solidified liquid crystal layer 130 may be interposed between the substrate 110 and the color filter layer 120.

FIG. 5 is a sectional view schematically showing a retardation substrate according to a modified example. This retardation substrate 10 is the same as the retardation substrate 10 described with reference to FIGS. 1 to 4 except that the solidified liquid crystal layer 130 is interposed between the substrate 110 and the color filter layer 120.

In the case where such a structure is employed, for example, in a liquid crystal display including the retardation layer 10, the solidified liquid crystal layer 130 does not suppress the inclusion of impurities from the color filter layer 120 into the liquid crystal layer. However, in the case where this structure is employed, there is no possibility that the color filter layer 120 is subjected to the exposure process and the heat treatment process for forming the solidified liquid crystal layer 130. Therefore, in the case where such a structure is employed, deteriorations of the color filter layer 120 due to the above-described exposure process and the heat treatment process are less prone to occur as compared with the case where the structure shown in FIGS. 1 and 2 is employed.

Further, in the case where this structure is employed, the color filter layer 120 can be formed on the solidified liquid crystal layer 130. Typically, the surface of the solidified liquid crystal layer 120 is roughly flat. Therefore, in this case, the color filter layer 120 that derivers the design performance can be obtained more easily as compared with the case where the color filter layer 120 is formed on a surface provided with a relief structure.

Typically, the solidified liquid crystal layer 130 has a uniform thickness. However, in particular cases, the regions 130 a to 130 c of the solidified liquid crystal layer 130 can be different in thickness from one another.

FIG. 6 is a sectional view schematically showing a solidified liquid crystal layer according to an example. FIG. 7 is a sectional view schematically showing a solidified liquid crystal layer according to another example. Note that in FIGS. 6 and 7, only the substrate 110 and the solidified liquid crystal layer 130 are depicted to omit the color filter layer 120 in the interests of simplicity.

The thickness of the solidified liquid crystal layer 130 shown in FIG. 6 is uniform almost throughout the layer. In contrast, in the solidified liquid crystal layer 130 shown in FIG. 7, the region 130 b is thinner than the region 130 a, while the region 130 c is thinner than the region 130 b. The reason why the structure shown in FIG. 7 is produced in particular cases is considered as follows.

Just after the first exposure process shown in FIG. 3, the region 130 b′ is higher in the unreacted compound content than the region 130 a′, while the region 130 c′ is higher in the unreacted compound content than the region 130 b′. In the case where the unreacted compound can easily migrate between the regions 130 a′ to 130 c′, a portion of the unreacted compound migrates from a region higher in its content to a region lower in its content. As a result, the structure shown in FIG. 7 is obtained.

The properties such as average molecular weight, viscosity and surface tension of the liquid crystal material layer or the process conditions such as exposure value in the first exposure process and temperature, rate of temperature increase, duration at target temperature and atmosphere in the first heat treatment process affect whether the structure shown in FIG. 7 is obtained or not, or affect to what extent each of the maximum thickness and the minimum thickness of the solidified liquid crystal layer 130 reaches in the case where the structure shown in FIG. 7 is obtained. However, in most cases, the difference between the maximum thickness and the minimum thickness of the solidified liquid crystal layer 130 is equal to or less than 25% of the average thickness of the solidified liquid crystal layer 130. Note that depending on the above-described properties and process conditions, the difference between the maximum thickness and the minimum thickness of the solidified liquid crystal layer 130 can reach 50% or more of the average thickness of the solidified liquid crystal layer 130.

The above-described retardation substrate 10 can be used for various applications. For example, the retardation substrate 10 can be used in display techniques typified by a liquid crystal display technique.

FIG. 8 is an example of a liquid crystal display that can be manufactured using the retardation substrate shown in FIGS. 1 and 2.

The liquid crystal display shown in FIG. 8 is a transmissive liquid crystal display employing an active matrix driving method. The liquid crystal display includes a color filter substrate 10′, an array substrate 20, a liquid crystal layer 30, a pair of polarizing plates 40, and a backlight (not shown).

The color filter substrate 10′ includes the retardation substrate 10 described above, a counter electrode 150, and an alignment layer 160.

The counter electrode 150 is formed on the solidified liquid crystal layer 130. It is a continuous film extending over the display area. The counter electrode 150 is made of the above-described transparent conductor, for example.

The alignment layer 160 covers the counter electrode 150. Forming a transparent layer of resin such as polyimide on the counter electrode 150 and subjecting the transparent resin layer to an alignment process such as rubbing process can obtain the alignment layer 160, for example. The alignment layer 160 may be formed using a photo-alignment technique.

The array substrate 20 includes a substrate 210 facing the alignment layer 160. The substrate 210 is a light-transmitting substrate such as glass plate or resin plate.

On the surface of the substrate 210 facing the alignment layer 160, pixel circuits (not shown), scanning lines (not shown), signal lines (not shown), and pixel electrodes 250 are arranged. The pixel circuits each includes a switching device such as thin-film transistor and are arranged in a matrix on the substrate. The scanning lines are arranged correspondingly with the rows of the pixel circuits. The operation of each pixel circuit is controlled by a scanning signal supplied via the scanning line. The signal lines are arranged correspondingly with the columns of the pixel circuits. Each pixel electrode 250 is connected to the signal line via the pixel circuit. Each pixel electrode 250 faces one of the coloring layers 120 a to 120 c.

The pixel electrodes 250 are covered with an alignment layer 260. Forming a transparent layer of resin such as polyimide on the pixel electrode 250 and subjecting the transparent resin layer to an alignment process such as rubbing process can obtain the alignment layer 260, for example. The alignment layer 260 may be formed using a photo-alignment technique.

The color filter substrate 10′ and the array substrate are bonded together via a frame-shaped adhesive layer (not shown). The color filter substrate 10′, the array substrate 20 and the adhesive layer form a hollow structure.

The liquid crystal layer 30 is made of a liquid crystal compound or a liquid crystal composition. The liquid crystal compound or the liquid crystal composition has flowability and fills the space enclosed with the color filter substrate 10′, the array substrate 20 and the adhesive layer. The color filer substrate 10′, the array substrate 20, the adhesive layer and the liquid crystal layer 30 form a liquid crystal cell.

The polarizing plates 40 are adhered to the main surfaces of the liquid crystal cell. The polarizing plates 40 are arranged such that their transmission axes intersect orthogonally, for example.

In the liquid crystal display, the regions 130 a to 130 c of the solidified liquid crystal layer 130 are almost equal in thickness to one another and are different in refractive index anisotropy from one another. Accordingly, it is possible to optimize the refractive index anisotropy of each of the regions 130 a to 130 c so as to achieve an ideal optical compensation for each of red, green and blue colors.

In addition, unavoidable variations in manufacturing conditions have a minimum effect on the surface profile of the solidified liquid crystal layer 130. Therefore, it is impossible that the unavoidable variations in the manufacturing conditions change the cell gap.

As described above, the retardation substrate 10 can be used in a transmissive liquid crystal display employing an active matrix driving method. The retardation substrate 10 can be used in other displays.

For example, the retardation substrate 10 may be used in a semi-transparent liquid crystal display or a reflective liquid crystal display. Also, driving methods other than an active matrix driving method such as passive matrix driving method may be employed in the liquid crystal display. Alternatively, the retardation substrate 10 may be used in displays other than liquid crystal displays such as organic electroluminescent display.

Examples of the present invention will be described below.

Note that in the following examples, all the operations handling photosensitive materials were performed under the illumination of a yellow or red lamp in order to prevent any undesirable light exposure.

First, the manufactures of alkaline developer-type colored resists used for forming color filer layers, the preparations of acrylic resin solutions and fluid dispersions of pigments used for manufacturing them, and manufactures of salt milling-treated pigments used for preparing the fluid dispersions of pigments will be described.

<Preparation of Acrylic Resin Solution 1>

370 parts by mass of cyclohexanone was charged into a reaction vessel and heated to 80° C. while supplying the vessel with nitrogen gas. The following mixture of monomers and the thermal polymerization initiator was dropped into the vessel for 1 hour while keeping the temperature of liquid in the vessel at the above temperature so as to cause the polymerization reaction.

Methacrylic acid 20.0 parts by mass Methyl methacrylate 10.0 parts by mass n-butyl methacrylate 55.0 parts by mass 2-hydroxyethyl methacrylate 15.0 parts by mass 2,2′-azobisisobutyronitrile  4.0 parts by mass

After the dropping, the reaction was continued at 80° C. for additional 3 hours. Thereafter, a solution prepared by dissolving 1.0 part by mass of azobisisobutyronitrile in 50 parts by mass of cyclohexanone was added to the liquid in the vessel, and the reaction was continued at 80° C. for additional 1 hour to obtain a solution of acrylic resin. The weight-average molecular weight of the acrylic resin was about 40,000.

After cooling to an ambient temperature, about 2 g of the above resin solution was taken as a sample. The sample was dried by heating at 180° C. for 20 minutes and a mass of nonvolatile matter was measured. Based on the results of the measurement, cyclohexanone was added to the above resin solution such that the concentration of the nonvolatile matter was 20% by mass. Thus, an acrylic resin solution 1 was prepared.

<Preparation of Acrylic Resin Solution 2>

370 parts by mass of cyclohexanone was charged into a reaction vessel and heated to 80° C. while supplying the vessel with nitrogen gas. The following mixture of monomers and the thermal polymerization initiator was dropped into the vessel for 1 hour while keeping the temperature of liquid in the vessel at the above temperature so as to cause the polymerization reaction.

Methacrylic acid 20.0 parts by mass Methyl methacrylate 10.0 parts by mass n-butyl methacrylate 35.0 parts by mass 2-hydroxyethyl methacrylate 15.0 parts by mass 2,2′-azobisisobutyronitrile  4.0 parts by mass Paracumylphenolethyleneoxide-modified acrylate 20.0 parts by mass (“ARONIX M110” manufactured by Toagosei Co., Ltd.)

After the dropping, the reaction was continued at 80° C. for additional 3 hours. Thereafter, a solution prepared by dissolving 1.0 part by mass of azobisisobutyronitrile in 50 parts by mass of cyclohexanone was added to the liquid in the vessel, and the reaction was continued at 80° C. for additional 1 hour to obtain a solution of acrylic resin. The weight-average molecular weight of the acrylic resin was about 40,000.

After cooling to an ambient temperature, about 2 g of the above resin solution was taken as a sample. The sample was dried by heating at 180° C. for 20 minutes and a mass of nonvolatile matter was measured. Based on the results of the measurement, cyclohexanone was added to the above resin solution such that the concentration of the nonvolatile matter was 20% by mass. Thus, an acrylic resin solution 2 was prepared.

<Preparation of Acrylic Resin Solution 3>

560 parts by mass of cyclohexanone was charged into a reaction vessel and heated to 80° C. while supplying the vessel with nitrogen gas. The following mixture of monomers and the thermal polymerization initiator was dropped into the vessel for 1 hour while keeping the temperature of liquid in the vessel at the above temperature so as to cause the polymerization reaction.

Methacrylic acid 34.0 parts by mass Methyl methacrylate 23.0 parts by mass n-butyl methacrylate 45.0 parts by mass 2-hydroxyethyl methacrylate 70.5 parts by mass 2,2′-azobisisobutyronitrile  8.0 parts by mass

After the dropping, the reaction was continued at 1000° C. for additional 3 hours. Thereafter, a solution prepared by dissolving 1.0 part by mass of azobisisobutyronitrile in 55 parts by mass of cyclohexanone was added to the liquid in the vessel, and the reaction was continued at 80° C. for additional 1 hour to obtain a solution of copolymer.

Next, the following mixture of compounds was dropped into 338 parts by mass of the copolymer solution thus obtained at 70° C. for 3 hours.

2-methacroyl ethylisocyanate 32.0 parts by mass Dibutyltin laurate 0.4 parts by mass Cyclohexanone 120.0 parts by mass

After cooling to an ambient temperature, about 2 g of the above resin solution was taken as a sample. The sample was dried by heating at 180° C. for 20 minutes and a mass of nonvolatile matter was measured. Based on the results of the measurement, cyclohexanone was added to the above resin solution such that the concentration of the nonvolatile matter was 20% by mass. Thus, an acrylic resin solution 3 was prepared. The acrylic resin had a weight-average molecular weight of 20,000 and a double bond equivalent of 470.

<Preparation of Acrylic Resin Solution 4>

560 parts by mass of cyclohexanone was charged into a reaction vessel and heated to 80° C. while supplying the vessel with nitrogen gas. The following mixture of monomers and the thermal polymerization initiator was dropped into the vessel for 1 hour while keeping the temperature of liquid in the vessel at the above temperature so as to cause the polymerization reaction.

Methacrylic acid 34.0 parts by mass Methyl methacrylate 23.0 parts by mass n-butyl methacrylate 25.0 parts by mass 2-hydroxyethyl methacrylate 70.5 parts by mass 2,2′-azobisisobutyronitrile  8.0 parts by mass Paracumylphenolethyleneoxide-modified acrylate 20.0 parts by mass (“ARONIX M110” manufactured by Toagosei Co., Ltd.)

After the dropping, the reaction was continued at 100° C. for additional 3 hours. Thereafter, a solution prepared by dissolving 1.0 part by mass of azobisisobutyronitrile in 55 parts by mass of cyclohexanone was added to the liquid in the vessel, and the reaction was continued at 80° C. for additional 1 hour to obtain a solution of copolymer.

Next, the following mixture of compounds was dropped into 338 parts by mass of the copolymer solution thus obtained at 70° C. for 3 hours.

2-methacroyl ethylisocyanate  32.0 parts by mass Dibutyltin laurate  0.4 parts by mass Cyclohexanone 120.0 parts by mass

After cooling to an ambient temperature, about 2 g of the above resin solution was taken as a sample. The sample was dried by heating at 180° C. for 20 minutes and a mass of nonvolatile matter was measured. Based on the results of the measurement, cyclohexanone was added to the above resin solution such that the concentration of the nonvolatile matter was 20% by mass. Thus, an acrylic resin solution 4 was prepared. The acrylic resin had a weight-average molecular weight of 20,000 and a double bond equivalent of 470.

<Manufacture of Salt Milling-Treated Red Pigment>

200 parts by mass of red pigment (C. I. pigment red 254: “IRGAPHOR RED B-CF” manufactured by Ciba Specialty Chemicals, Inc.), 1,400 parts by mass of sodium chloride, and 360 parts by mass of diethylene glycol were charged into a 1-gallon kneader of stainless steel (manufactured by Inoue Manufacturing Co., Ltd.) and kneaded at 80° C. for 6 hours. Then, the kneaded product was added into 8 liters of hot water and the mixture was stirred for 2 hours while heating at 80° C. so as to obtain slurry. Filtrations of the slurry and washings of filter cake by water were repeated to remove sodium chloride and diethylene glycol from the pigment. After that, the filter cake was dried at 85° C. for a whole day and night to obtain 190 parts by mass of “Treated pigment of P. R. 254”.

<Manufacture of Salt Milling-Treated Green Pigment>

“Treated pigment of P. G. 36” was obtained by the same method as that described for the salt milling-treated red pigment except that green pigment (C. I. pigment green 36: “LIONOL GREEN 6YK” manufactured by Toyo Ink Manufacturing Co., Ltd.) was used instead of the red pigment.

<Manufacture of Salt Milling-Treated Yellow Pigment>

“Treated pigment of P. Y. 138” was obtained by the same method as that described for the salt milling-treated red pigment except that yellow pigment (C. I. pigment yellow 138: “LIONOL YELLOW 1030” manufactured by Toyo Ink Manufacturing Co., Ltd.) was used instead of the red pigment.

<Manufacture of Salt Milling-Treated Blue Pigment>

“Treated pigment of P. B. 15:6” was obtained by the same method as that described for the salt milling-treated red pigment except that blue pigment (C. I. pigment blue 15:6: “HELIOGEN BLUE L-6700F” manufactured by BASF Corp.) was used instead of the red pigment.

<Manufacture of Salt Milling-Treated Violet Pigment>

“Treated pigment of P. V. 23” was obtained by the same method as that described for the salt milling-treated red pigment except that blue pigment (C. I. pigment violet 23: “LIONOGEN VIOLET R6200” manufactured by Toyo Ink Manufacturing Co., Ltd.) was used instead of the red pigment.

<Preparation of Red Pigment Dispersion>

The following substances were stirred to obtain a homogenous mixture. The mixture was subjected to a process of 10 hours using an Eiger mill so as to uniformly disperse the solid content in the liquid. Here, zirconia beads having a diameter of 0.5 mm were used as grinding media. Then, the dispersion was filtrated to obtain red pigment dispersion. For the filtration, used was a filter capable of separating particles having a diameter of 1.0 μm or larger from liquid phase.

Treated pigment of P. R. 254  8.0 parts by mass Dispersing agent (“SOLSPARS 20000” 1.0 part by mass manufactured by Avecia Corp.) Acrylic resin solution 1 40.0 parts by mass Cyclohexanone 51.0 parts by mass

<Preparation of Green Pigment Dispersion>

The following substances were stirred to obtain a homogenous mixture. The mixture was subjected to a process of 10 hours using an Eiger mill so as to uniformly disperse the solid content in the liquid. Here, zirconia beads having a diameter of 0.5 mm were used as grinding media. Then, the dispersion was filtrated to obtain green pigment dispersion. For the filtration, used was a filter capable of separating particles having a diameter of 1.0 μm or larger from liquid phase.

Treated pigment of P. G. 36  8.0 parts by mass Dispersing agent (“SOLSPARS 20000” 1.0 part by mass manufactured by Avecia Corp.) Acrylic resin solution 1 40.0 parts by mass Cyclohexanone 51.0 parts by mass

<Preparation of Yellow Pigment Dispersion>

The following substances were stirred to obtain a homogenous mixture. The mixture was subjected to a process of 10 hours using an Eiger mill so as to uniformly disperse the solid content in the liquid. Here, zirconia beads having a diameter of 0.5 mm were used as grinding media. Then, the dispersion was filtrated to obtain yellow pigment dispersion. For the filtration, used was a filter capable of separating particles having a diameter of 1.0 μm or larger from liquid phase.

Treated pigment of P. Y. 138  8.0 parts by mass Dispersing agent (“SOLSPARS 20000” 1.0 part by mass manufactured by Avecia Corp.) Acrylic resin solution 1 40.0 parts by mass Cyclohexanone 51.0 parts by mass

<Preparation of Blue Pigment Dispersion>

The following substances were stirred to obtain a homogenous mixture. The mixture was subjected to a process of 10 hours using an Eiger mill so as to uniformly disperse the solid content in the liquid. Here, zirconia beads having a diameter of 0.5 mm were used as grinding media. Then, the dispersion was filtrated to obtain blue pigment dispersion. For the filtration, used was a filter capable of separating particles having a diameter of 1.0 μm or larger from liquid phase.

Treated pigment of P. B. 15:6  8.0 parts by mass Dispersing agent (“BYK 111” manufactured 1.0 part by mass by BYK-CHEMIE GmbH) Acrylic resin solution 2 40.0 parts by mass Cyclohexanone 51.0 parts by mass

<Preparation of Violet Pigment Dispersion>

The following substances were stirred to obtain a homogenous mixture. The mixture was subjected to a process of 10 hours using an Eiger mill so as to uniformly disperse the solid content in the liquid. Here, zirconia beads having a diameter of 0.5 mm were used as grinding media. Then, the dispersion was filtrated to obtain violet pigment dispersion. For the filtration, used was a filter capable of separating particles having a diameter of 1.0 μm or larger from liquid phase.

Treated pigment of P. V. 23  8.0 parts by mass Dispersing agent (“BYK 111” manufactured by 1.0 part by mass BYK-CHEMIE GmbH) Acrylic resin solution 2 40.0 parts by mass Cyclohexanone 51.0 parts by mass

<Manufacture of Red Coloring Composition>

The following substances were stirred to obtain a homogenous mixture. The mixture was filtrated to obtain an alkaline developer-type red coloring composition. For the filtration, used was a filter capable of separating particles having a diameter of 0.6 μm or larger from liquid phase.

Red pigment dispersion 50.0 parts by mass Acrylic resin solution 3 10.0 parts by mass Trimethylolpropane triacrylate (“NK ESTER 3.0 parts by mass A-TMPT” manufactured by Shin-Nakamura Chemical Co., LTD.) Photo-polymerization initiator (“Irgacure 907” 1.8 parts by mass manufactured by Ciba Specialty Chemicals Inc.) Sensitizer (“EAB-F” manufactured by Hodogaya 0.2 parts by mass Chemical Co., Ltd.) Cyclohexanone 10.0 parts by mass

<Manufacture of Green Coloring Composition>

The following substances were stirred to obtain a homogenous mixture. The mixture was filtrated to obtain an alkaline developer-type red coloring composition. For the filtration, used was a filter capable of separating particles having a diameter of 0.6 μm or larger from liquid phase.

Green pigment dispersion 30.0 parts by mass Yellow pigment dispersion 20.0 parts by mass Acrylic resin solution 3 10.0 parts by mass Trimethylolpropane triacrylate (“NK ESTER 3.0 parts by mass A-TMPT” manufactured by Shin-Nakamura Chemical Co., LTD.) Photo-polymerization initiator (“Irgacure 907” 1.8 parts by mass manufactured by Ciba Specialty Chemicals Inc.) Sensitizer (“EAB-F” manufactured by Hodogaya 0.2 parts by mass Chemical Co., Ltd.) Cyclohexanone 10.0 parts by mass

<Manufacture of Blue Coloring Composition>

The following substances were stirred to obtain a homogenous mixture. The mixture was filtrated to obtain an alkaline developer-type red coloring composition. For the filtration, used was a filter capable of separating particles having a diameter of 0.6 μm or larger from liquid phase.

Blue pigment dispersion 45.0 parts by mass Violet pigment dispersion 5.0 parts by mass Acrylic resin solution 4 10.0 parts by mass Trimethylolpropane triacrylate (“NK ESTER 3.0 parts by mass A-TMPT” manufactured by Shin-Nakamura Chemical Co., LTD.) Photo-polymerization initiator (“Irgacure 907” 1.8 parts by mass manufactured by Ciba Specialty Chemicals Inc.) Sensitizer (“EAB-F” manufactured by Hodogaya 0.2 parts by mass Chemical Co., Ltd.) Cyclohexanone 10.0 parts by mass

Example 1

The above-described red coloring composition was applied to a glass substrate using a spin coater at a dried thickness of 2.0 μm. Note that the glass substrate used herein was optically isotropic. Next, the coated film was dried by heating at 70° C. for 20 minutes using a clean oven. After cooling the substrate to an ambient temperature, the coated film was irradiated with ultraviolet ray through a photomask. An extra-high-pressure mercury-vapor lamp was used as a source of the ultraviolet ray. Then, the coated film was subjected to a spray developing using an aqueous solution of sodium carbonate at 23° C. Thereafter, the coated film was washed by deionized water and air-dried. Further, the coated film was fired at 230° C. for 30 minutes using a clean oven. A red coloring layer was thus formed on the substrate.

Next, a green coloring layer was further formed on the substrate on which the red coloring layer had been formed by the same method as that described for the red coloring composition except that the green coloring composition was used instead of the red coloring composition. Thereafter, a blue coloring layer was further formed on the substrate on which the red coloring layer and the green coloring layer had been formed by the same method as that described for the red coloring composition except that the blue coloring composition was used instead of the red coloring composition. A color filter layer was thus obtained.

The thickness direction retardation R_(th) was determined for the layered product of the color filer layer and the glass substrate. As a result, at the portion corresponding to the red coloring layer, the retardation R_(th) for the light having a wavelength of 630 nm was 27 nm. At the portion corresponding to the green coloring layer, the retardation R_(th) for the light having a wavelength of 550 nm was −18 nm. At the portion corresponding to the blue coloring layer, the retardation R_(th) for the light having a wavelength of 450 nm was 2 nm.

Note that a thickness direction retardation R_(th) for a certain coloring layer can be calculated using in-plane refractive indices n_(x) and n_(y) and a thickness direction refractive index n_(z) at one of wavelengths of light that the coloring layer transmits, for example, a center wavelength and the thickness d of the coloring layer. To be more specific, the thickness direction retardation R_(th) is the difference between the average of the refractive indices n_(x) and n_(y) and the refractive index n_(z) multiplied by the thickness d, i.e., the product [(n_(x)−n_(y))/2−n_(z)]×d.

Next, the following substances were stirred to obtain a homogenous mixture. The mixture was filtrated to obtain a coating solution. For the filtration, used was a filter capable of separating particles having a diameter of 0.6 μm or larger from liquid phase.

Vertically oriented polymerizable liquid crystal 19.0 parts by mass (“UCL-018” manufactured by Dainippon Ink and Chemicals, Inc.) Photo-polymerization initiator (“Irgacure 907” 1.0 part by mass manufactured by Ciba Specialty Chemicals Inc.) Surfactant (cyclohexanone-solution of “BYK 111”  3.0 parts by mass manufactured by BYK-CHEMIE GmbH with a concentration of 2%) Cyclohexanone 77.0 parts by mass

The coating solution was applied to the color filter layer using a spin coater at a dried thickness of 0.7 μm. Subsequently, the coated film was dried by heating at 90° C. for 2 minutes using a hot plate. A liquid crystal material layer was thus formed on the color filter layer.

Then, each of the regions of the liquid crystal material layer corresponding to the red coloring layer, the green coloring layer and the blue coloring layer was irradiated with ultraviolet ray through a photomask. An extra-high-pressure mercury-vapor lamp was used as a source of the ultraviolet ray. The exposure value for the region corresponding to the red coloring layer was 500 mJ/cm², the exposure value for the region corresponding to the green coloring layer was 5 mJ/cm², and the exposure value for the region corresponding to the blue coloring layer was 20 mj/cm².

Thereafter, the liquid crystal material layer was heated at 80° C. in a nitrogen atmosphere using a hot plate. Subsequently, the entire liquid crystal material layer was irradiated with the ultraviolet ray while keeping the temperature at 80° C. so as to obtain a solidified liquid crystal layer. A retardation substrate was thus manufactured.

The thickness direction retardation R_(th) was determined for the retardation substrate. As a result, at the portion corresponding to the red coloring layer, the retardation R_(th) for the light having a wavelength of 630 nm was −81 nm. At the portion corresponding to the green coloring layer, the retardation R_(th) for the light having a wavelength of 550 nm was −80 nm. At the portion corresponding to the blue coloring layer, the retardation R_(th) for the light having a wavelength of 450 nm was −81 nm. The results are summarized in the following TABLE 1.

TABLE 1 Red Green Blue Exposure value in first exposure process 500 mJ/cm² 5 mJ/cm² 20 mJ/cm² Wavelength for determining retardation 630 nm 550 nm 450 nm Thickness direction Color filter layer 27 nm −18 nm 2 nm retardation Retardation substrate −81 nm −80 nm −81 nm Solidified liquid −108 nm −62 nm −83 nm crystal layer Thickness of solidified liquid crystal layer 0.7 μm 0.7 μm 0.7 μm Birefringence Δn of solidified liquid 0.151 0.088 0.120 crystal layer

Note that in TABLE 1, “Red” indicates the red coloring layer, the region of the solidified liquid crystal layer corresponding to the red coloring layer, or the portion of the retardation substrate corresponding to the red coloring layer. “Green” indicates the green coloring layer, the region of the solidified liquid crystal layer corresponding to the green coloring layer, or the portion of the retardation substrate corresponding to the green coloring layer. “Blue” indicates the blue coloring layer, the region of the solidified liquid crystal layer corresponding to the blue coloring layer, or the portion of the retardation substrate corresponding to the blue coloring layer.

Example 2

A color filter layer was formed on a glass substrate by the same method as that described in Example 1.

Next, the following substances were stirred to obtain a homogenous mixture. The mixture was filtrated to obtain a coating solution. For the filtration, used was a filter capable of separating particles having a diameter of 0.6 μm or larger from liquid phase.

Horizontally oriented polymerizable liquid crystal 18.3 parts by mass  (“PALIOCOLOR LC 242” manufactured by BASF Japan Corp.) Chiral agent (“PALIOCOLOR LC 756” 1.5 parts by mass manufactured by BASF Japan Corp.) Photo-polymerization initiator (“Irgacure 907” 0.2 parts by mass manufactured by Ciba Specialty Chemicals Inc.) Surfactant (cyclohexanone-solution of “BYK 111” 3.0 parts by mass manufactured by BYK-CHEMIE GmbH with a concentration of 2%) Cyclohexanone 77.0 parts by mass 

The coating solution was applied to the color filter layer using a spin coater at a dried thickness of 3.3 μm. Subsequently, the coated film was dried by heating at 90° C. for 2 minutes using a hot plate. A liquid crystal material layer was thus formed on the color filter layer.

Then, each of the regions of the liquid crystal material layer corresponding to the red coloring layer, the green coloring layer and the blue coloring layer was irradiated with ultraviolet ray through a photomask. An extra-high-pressure mercury-vapor lamp was used as a source of the ultraviolet ray. The exposure value for the region corresponding to the red coloring layer was 50 mJ/cm², the exposure value for the region corresponding to the green coloring layer was 500 mJ/cm², and the exposure value for the region corresponding to the blue coloring layer was 200 mJ/cm².

Thereafter, the liquid crystal material layer was fired at 230° C. for 40 minutes using a clean oven so as to obtain a solidified liquid crystal layer. A retardation substrate was thus manufactured.

The thickness direction retardation R_(th) was determined for the retardation substrate. As a result, at the portion corresponding to the red coloring layer, the retardation R_(th) for the light having a wavelength of 630 nm was 152 nm. At the portion corresponding to the green coloring layer, the retardation R_(th) for the light having a wavelength of 550 nm was 150 nm. At the portion corresponding to the blue coloring layer, the retardation R_(th) for the light having a wavelength of 450 nm was 152 nm. The results are summarized in the following TABLE 2.

TABLE 2 Red Green Blue Exposure value in first exposure process 50 mJ/cm² 500 mJ/cm² 200 mJ/cm² Wavelength for determining retardation 630 nm 550 nm 450 nm Thickness direction Color filter layer 27 nm −18 nm 2 nm retardation Retardation substrate 152 nm 150 nm 152 nm Solidified liquid 125 nm 168 nm 150 nm crystal layer Thickness of solidified liquid crystal 3.1 μm 3.3 μm 3.2 μm layer Birefringence Δn of solidified liquid 0.040 0.051 0.047 crystal layer

Example 3

The above-described red coloring composition was applied to a glass substrate using a spin coater at a dried thickness of 1.0 μm. Note that the glass substrate used herein was optically isotropic. Next, the coated film was dried by heating at 70° C. for 20 minutes using a clean oven. After cooling the substrate to an ambient temperature, the coated film was irradiated with ultraviolet ray through a photomask. An extra-high-pressure mercury-vapor lamp was used as a source of the ultraviolet ray. Then, the coated film was subjected to a spray developing using an aqueous solution of sodium carbonate at 23° C. Thereafter, the coated film was washed by deionized water and air-dried. Further, the coated film was fired at 230° C. for 30 minutes using a clean oven. A red coloring layer was thus formed on the substrate.

Next, a green coloring layer was further formed on the substrate on which the red coloring layer had been formed by the same method as that described for the red coloring composition except that the green coloring composition was used instead of the red coloring composition. Thereafter, a blue coloring layer was further formed on the substrate on which the red coloring layer and the green coloring layer had been formed by the same method as that described for the red coloring composition except that the blue coloring composition was used instead of the red coloring composition. A color filter layer was thus obtained.

The thickness direction retardation R_(th) was determined for the layered product of the color filer layer and the glass substrate. As a result, the retardation R_(th) for the light having a wavelength of 630 nm at the portion corresponding to the red coloring layer, the retardation R_(th) for the light having a wavelength of 550 nm at the portion corresponding to the green coloring layer, and the retardation R_(th) for the light having a wavelength of 450 nm at the portion corresponding to the blue coloring layer were zero.

Next, a material of alignment layer (“SE-1410” manufactured by Nissan Chemical Industries, Ltd.) was applied to the color filter layer using a spin coater at a dried thickness of 0.1 μm. Then, the coated film was fired at 230° C. for 40 minutes using a clean oven. Further, the coated film was subjected to a rubbing process in a direction parallel with a main surface thereof so as to obtain an alignment layer.

Next, the following substances were stirred to obtain a homogenous mixture. The mixture was filtrated to obtain a coating solution. For the filtration, used was a filter capable of separating particles having a diameter of 0.6 μm or larger from liquid phase.

Horizontally oriented polymerizable liquid crystal 39.7 parts by mass (“PALIOCOLOR LC 242” manufactured by BASF Japan Corp.) Photo-polymerization initiator (“Irgacure 907” 0.3 part by mass manufactured by Ciba Specialty Chemicals Inc.) Surfactant (cyclohexanone-solution of 6.0 parts by mass “BYK 111” manufactured by BYK-CHEMIE GmbH with a concentration of 2%) Cyclohexanone 154.0 parts by mass

The coating solution was applied to the alignment layer using a spin coater at a dried thickness of 1.6 μm. Subsequently, the coated film was dried by heating at 90° C. for 2 minutes using a hot plate. A liquid crystal material layer was thus formed on the alignment layer.

Then, each of the regions of the liquid crystal material layer corresponding to the red coloring layer, the green coloring layer and the blue coloring layer was irradiated with ultraviolet ray through a photomask. An extra-high-pressure mercury-vapor lamp was used as a source of the ultraviolet ray. The exposure value for the region corresponding to the red coloring layer was 500 mJ/cm², the exposure value for the region corresponding to the green coloring layer was 200 mJ/cm², and the exposure value for the region corresponding to the blue coloring layer was 5 mJ/cm².

Thereafter, the liquid crystal material layer was fired at 230° C. for 40 minutes using a clean oven so as to obtain a solidified liquid crystal layer. A retardation substrate was thus manufactured.

The thickness direction retardation R_(th) was determined for the retardation substrate. As a result, at the portion corresponding to the red coloring layer, the retardation R_(th) for the light having a wavelength of 630 nm was 161 nm. At the portion corresponding to the green coloring layer, the retardation R_(th) for the light having a wavelength of 550 nm was 136 nm. At the portion corresponding to the blue coloring layer, the retardation R_(th) for the light having a wavelength of 450 nm was 112 nm. The results are summarized in the following TABLE 3.

TABLE 3 Red Green Blue Exposure value in first exposure process 500 mJ/cm² 200 mJ/cm² 5 mJ/cm² Wavelength for determining retardation 630 nm 550 nm 450 nm Thickness direction Color filter layer 0 nm 0 nm 0 nm retardation Retardation substrate 161 nm 136 nm 112 nm Solidified liquid 161 nm 136 nm 112 nm crystal layer Thickness of solidified liquid crystal 1.6 μm 1.6 μm 1.5 μm layer Birefringence Δn of solidified liquid 0.100 0.085 0.072 crystal layer

Additional advantages and modifications will readily occur to those skilled in the art. Therefore, the invention in its broader aspects is not limited to the specific details and representative embodiments shown and described herein. Accordingly, various modifications may be made without departing from the spirit or scope of the general inventive concept as defined by the appended claims and their equivalents. 

1-17. (canceled)
 18. A retardation substrate comprising: a substrate; and a solidified liquid crystal layer placed on the substrate, the solidified liquid crystal layer having an optical anisotropy, the solidified liquid crystal layer being provided such that it includes a region in a low orientation state and a region in a high orientation state having different refractive index anisotropies due to different degrees of orientation, and the solidified liquid crystal layer being formed by subjecting a liquid crystal phase to a heating process at or higher than a temperature at which a phase transition to an isotropic phase occurs.
 19. The retardation substrate according to claim 18, wherein the solidified liquid crystal layer is a continuous layer.
 20. The retardation substrate according to claim 18, wherein the solidified liquid crystal layer is formed by polymerizing and/or crosslinking a compound including a thermotropic liquid crystal.
 21. The retardation substrate according to claim 18, wherein one of glass, plastic and film substrates is used as the substrate.
 22. The retardation substrate according to claim 18, wherein the solidified liquid crystal layer has predetermined retardations for respective colors such that incident lights transmitted by a color filter are optically compensated for respective colors of the opposing color filter.
 23. The retardation substrate according to claim 18, wherein the solidified liquid crystal layer has a uniform thickness.
 24. The retardation substrate according to claim 18, wherein a thin film transistor (TFT) is provided between the solidified liquid crystal layer and the substrate.
 25. The retardation substrate according to claim 18, wherein a thin file transistor (TFT) is further provided above the solidified liquid crystal layer.
 26. A liquid crystal display comprising: a retardation substrate including a substrate; and a solidified liquid crystal layer placed on the substrate, the solidified liquid crystal layer having an optical anisotropy, the solidified liquid crystal layer being provided such that it includes a region in a low orientation state and a region in a high orientation state having different refractive index anisotropies due to different degrees of orientation, and the solidified liquid crystal layer being formed by subjecting a liquid crystal phase to a heating process at or higher than a temperature at which a phase transition to an isotropic phase occurs.
 27. A retardation substrate constituted at least by a substrate and a solidified liquid crystal layer produced by a manufacturing method including: applying a solution containing a compound having properties of thermotropic liquid crystal and polymerizable and/or crosslinkable in a photo-induced manner on a substrate to form a thin film in a state where the liquid crystal compound is aligned in a predetermined direction; irradiating the substrate with light such that regions thereof have different exposure values so as to make uncured-residue contents of the regions different correspondingly with the exposure values; heating the liquid crystal compound at or higher than a temperature at which a phase transition to an isotropic phase occurs; and curing the uncured liquid crystal compound to obtain a solidified liquid crystal layer including a low orientation region and a high orientation region.
 28. The retardation substrate according to claim 27, wherein one of glass, plastic and film substrates is used as the substrate.
 29. The retardation substrate according to claim 27, wherein the solidified liquid crystal layer has predetermined retardations for respective colors such that incident lights transmitted by a color filter are optically compensated for respective colors of the opposing color filter.
 30. The retardation substrate according to claim 27, wherein the solidified liquid crystal layer has a uniform thickness.
 31. The retardation substrate according to claim 27, wherein a thin film transistor (TFT) is provided between the solidified liquid crystal layer and the substrate.
 32. The retardation substrate according to claim 27, wherein a thin film transistor (TFT) is further provided above the solidified liquid crystal layer.
 33. A liquid crystal display comprising: a retardation substrate constituted at least by a substrate and a solidified liquid crystal layer produced by a manufacturing method including applying a solution containing a compound having properties of thermotropic liquid crystal and polymerizable and/or crosslinkable in a photo-induced manner on a substrate to form a thin film in a state where the liquid crystal compound is aligned in a predetermined direction, irradiating the substrate with light such that regions thereof have different exposure values so as to make uncured-residue contents of the regions different correspondingly with the exposure values, heating the liquid crystal compound at or higher than a temperature at which a phase transition to an isotropic phase occurs, and curing the uncured liquid crystal compound to obtain a solidified liquid crystal layer including a low orientation region and a high orientation region.
 34. A retardation substrate constituted at least by a substrate and a solidified liquid crystal layer formed by a manufacturing method including: applying a solution containing a compound having properties of thermotropic liquid crystal and polymerizable and/or crosslinkable in a photo-induced manner on a substrate to form a thin film in a state where the liquid crystal compound is aligned in a predetermined direction; irradiating the substrate with light such that regions thereof have different exposure values so as to make uncured-residue contents of the regions different correspondingly with the exposure values; heating the liquid crystal compound at or higher than a temperature at which a phase transition to an isotropic phase occurs; and exposing whole the substrate to light while keeping it at or higher than a temperature at which the liquid crystal compound is kept in the isotropic phase to obtain a solidified liquid crystal layer including a region in a low orientation state and a region in a high orientation state.
 35. The retardation substrate according to claim 34, wherein one of glass, plastic and film substrates is used as the substrate.
 36. The retardation substrate according to claim 34, wherein the solidified liquid crystal layer has predetermined retardations for respective colors such that incident lights transmitted by a color filter are optically compensated for respective colors of the opposing color filter.
 37. The retardation substrate according to claim 34, wherein the solidified liquid crystal layer has a uniform thickness.
 38. The retardation substrate according to claim 34, wherein a thin film transistor (TFT) is provided between the solidified liquid crystal layer and the substrate.
 39. The retardation substrate according to claim 34, wherein a thin film transistor (TFT) is further provided above the solidified liquid crystal layer.
 40. A liquid crystal display comprising: a retardation substrate constituted at least by a substrate and a solidified liquid crystal layer formed by a manufacturing method including applying a solution containing a compound having properties of thermotropic liquid crystal and polymerizable and/or crosslinkable in a photo-induced manner on a substrate to form a thin film in a state where the liquid crystal compound is aligned in a predetermined direction, irradiating the substrate with light such that regions thereof have different exposure values so as to make uncured-residue contents of the regions different correspondingly with the exposure values, heating the liquid crystal compound at or higher than a temperature at which a phase transition to an isotropic phase occurs, and exposing whole the substrate to light while keeping it at or higher than a temperature at which the liquid crystal compound is kept in the isotropic phase to obtain a solidified liquid crystal layer including a region in a low orientation state and a region in a high orientation state.
 41. A method of manufacturing a retardation substrate including a substrate and a solidified liquid crystal layer placed on the substrate, comprising the steps of: (a) applying on the substrate a solution containing a compound that exhibits properties of thermotropic liquid crystal and is polymerizable and/or crosslinkable in a photo-induced manner so as to form a film in a state where the liquid crystalline compound is oriented in a predetermined direction; (b) irradiating the liquid crystalline compound with light such that regions having different exposure values are produced so as to make uncured-residue contents of the regions different correspondingly with the exposure values; (c) heating the substrate at or higher than a phase transition temperature at which the liquid crystalline compounds changes to an isotropic phase; and (d) irradiating the whole substrate with light while keeping a temperature high enough for the liquid crystal compound to be maintained in the isotropic phase so as to form a solidified liquid crystal layer including a region in a low orientation state and a region in a high orientation state.
 42. The method according to claim 41, wherein the step (a) is performed such that the film has a uniform thickness throughout the substrate.
 43. The method according to claim 41, wherein a thin film transistor (TFT) is formed above the substrate before performing the step (a).
 44. The method according to claim 41, wherein a thin film transistor (TFT) is formed above the substrate after performing the step (d).
 45. A method of manufacturing a retardation substrate including a substrate and a solidified liquid crystal layer placed on the substrate, comprising the steps of: (a) applying on the substrate a solution containing a compound that exhibits properties of thermotropic liquid crystal and is polymerizable and/or crosslinkable in both photo-induced and heat-induced manners so as to form a film in a state where the liquid crystalline compound is oriented in a predetermined direction; (b) irradiating the liquid crystalline compound with light such that regions having different exposure values are produced so as to make uncured-residue contents of the regions different correspondingly with the exposure values; and (c) heating the substrate to a temperature equal to or higher than a phase transition temperature at which the liquid crystalline compounds changes to an isotropic phase and high enough for polymerization and/or crosslinking to occur so as to form a solidified liquid crystal layer including a region in a low orientation state and a region in a high orientation state.
 46. The method according to claim 45, wherein a thin film transistor (TFT) is formed above the substrate before performing the step (a).
 47. The method according to claim 45, wherein a thin film transistor (TFT) is formed above the substrate after performing the step (d).
 48. A method of manufacturing a retardation substrate including a substrate and a solidified liquid crystal layer placed on the substrate, comprising the steps of: (a) applying on the substrate a solution containing a compound that exhibits properties of thermotropic liquid crystal and is polymerizable and/or crosslinkable in a photo-induced manner so as to form a film in which the liquid crystalline compound is oriented in a predetermined direction; (b) irradiating the liquid crystalline compound with light such that regions having different exposure values are produced so as to make uncured-residue contents of the regions different correspondingly with the exposure values; (c) heating the substrate at or higher than a phase transition temperature at which the liquid crystalline compounds changes to an isotropic phase; and (d) irradiating a portion other than a region irradiated with light at a maximum exposure value in step (b) with light while keeping a temperature high enough for the liquid crystal compound to be maintained in the isotropic phase so as to form a solidified liquid crystal layer including a region in a low orientation state, a region in a high orientation state, and a region in a non-orientation state.
 49. The method according to claim 48, wherein an exposure value of each of the regions in step (d) is set such that a sum of the exposure values in steps (d) and (b) is equal to that of the region to which the light exposure is performed at the maximum exposure value in the step (b).
 50. The method according to claim 48, wherein a thin film transistor (TFT) is formed above the substrate before performing the step (a).
 51. The method according to claim 48, wherein a thin film transistor (TFT) is formed above the substrate after performing the step (d). 